热磨损的英文

• thermal wear
• thermic wear

• 磨损:    wear and tear; abrasive wear ...
• 热磨:    defibrating; hot-grinding
• 热磨合:    hot breaking-in; hot running-in
• 热磨机:    defibrater; defibrator; prefiner; thermofiner
• 磨损:    wear and tear; abrasive wear; abrase; abrade; detrition; wear; scuff; wear-out; fray; battering; abrade wear; abrasion; attrition wear; defacement; excoriate; foreworn; wear down; wearing; wornout 我的鞋跟给磨损了。 the heels of my shoes have (been) worn down. 这辆卡车基本上没有什么磨损。 the truck shows scarcely any sign of wear and tear.; 磨损程度 degree of wear; 磨损度 abradability; 磨损腐蚀试验 erosion corrosion test; 磨损检验 examine for wear; 磨损留量 wear allowance; tear-and-wear allowance; 磨损试验 [土] attrition test; abrasion test; 磨损试验机 abrasion tester; abrasive wear testing machine; wear-test machine; 磨损数据 wear data; 磨损速度 rate of wear; 磨损系数 coefficient of waste; coefficient of wear; wear coefficient; mortality factor; 磨损作用 abrasive action

例句与用法

1. Abstract : in the light of two common failure modes in use , i . e . thermal wear and hot fatigue crack , this paper analyzes the reasons and puts forward the measures to be taken for improving the life of forging die
   文摘:针对锻模在使用过程中常见的两种失效形式，即热磨损和热疲劳裂纹，分析了其产生的原因，并提出了为提高锻模寿命而应采取的措施。
2. With improvement of material composition and processing , the failure modes demonstrate predominately elevated wear and plastic deformation , and no earlier failure occurred , leading to a considerable improvement of service life and a stable number of 6000 ~ 7000 times , 80 % more than forging steel dies
   经改进材质及工艺后，热磨损、塑性变形为主要失效形式，而未出现早期断裂失效，寿命得到明显提高，稳定在6000 ~ 7000件，高于锻造模具钢80 %以上。

其他语言

热磨损的日语：ねつてきまもう